Pvb resin
PVB resin maka ihe nkiri PVB
PVB Resin maka MLCC, mkpuchi, inks, adver, wdg.
PVB resin maka ihe nkiri PVB
Ngwaahịa a nwere uru nke ụlọ ihe nkiri, adhesion, na-eguzogide, na-egbochi ihe nkiri, wdg, nke kwesịrị ekwesị maka iko nchekwa, photovoltaic na ubi ndị ọzọ.
Nkọwapụta teknụzụ
| Nọmba usoro n'usoro | Ihe | unit | DFS1719-03 |
| 1 | Mputa | Ntụ ntụ ọcha na enweghị adịghị ọcha | |
| 2 | Ọdịnaya ọdịnaya | % | ≤1.5 |
| 3 | Ọdịnaya Hydroxy | % | 17.0 ~ 20.0 |
| 4 | Bankyl Aldehyde ọdịnaya | % | 75.0 ~ 80.0 |
| 5 | Ọdịnaya acid | % | ≤0.0100 |
| 6 | 10.0wt% viscosity | MPA.S | 850 ~ 1250 |
| 7 | Nnukwu njupụta | g / 100ml | ≥14.0 |
PVB Resin maka MLCC, mkpuchi, inks, adver, wdg.
Ngwaahịa ndị a nwere ezigbo usoro ihe nkiri, na-agbanwe agbanwe, na-eguzogide ihu igwe, na-eguzogide ya na seramics ndị ọzọ, mkpuchi, na-acha na ubi ndị ọzọ.
Nkọwapụta teknụzụ
| Nọmba usoro n'usoro | 1 | 2 | 3 | 4 | 5 | 6 | 7 |
| Nkọwa na ụdị | Mputa | Mw | Ọdịnaya ọdịnaya | Bankyl Aldehyde ọdịnaya | Ọdịnaya Hydroxy | Ọdịnaya acid | Vissiosi(10% ngwọta na ethanol) |
| (/) | (%) | (wt%) | (wt%) | (%) | (MPA.S) | ||
| DFS0419-01 | Ntụ ntụ | 2.8 ~ 3.2 | ≤3.0 | 79 ± 3 | 18.0 ~ 21.0 | <0.05 | 30 ~ 60 |
| DFS0819-01 | Ntụ ntụ | 5.0 ~ 5.5 | ≤3.0 | 78 ± 3 | 17.0 ~ 21.0 | <0.05 | 100 ~ 220 |
| Dfm0319-a | Ntụ ntụ | 2.0 | ≤3.0 | 74 ± 3 | 18.0 ~ 21.0 | <0.05 | 10 ~ 30 |
| Dfm0321-a | Ntụ ntụ | 1.9 | ≤3.0 | 74 ± 3 | 19.0 ~ 22.0 | <0.05 | 10 ~ 30 |
| Dfm0812-a | Ntụ ntụ | 5.3 | ≤3.0 | > 85 | 10.5 ~ 13.0 | <0.05 | 120 ~ 180 |
| Dfm0815-a | Ntụ ntụ | 5.3 | ≤3.0 | 82 ± 3 | 13.0 ~ 16.0 | <0.05 | 80 ~ 150 |
| Dfm0819-a | Ntụ ntụ | 5.2 ~ 5.3 | ≤3.0 | 78 ± 3 | 18.0 ~ 20.0 | <0.05 | 100 ~ 170 |
| Dfm1519-a | Ntụ ntụ | 9.2 | ≤3.0 | 78 ± 3 | 18.0 ~ 21.0 | <0.05 | 40 ~ 90 * |
| Dfm1721-a | Ntụ ntụ | 11 | ≤3.0 | 75 + 3 | 19.0 ~ 22.0 | <0.05 | 60 ~ 120 * |